We offer aluminum alloy plate for mould 6061 T6 at good price and nice quality.
Dimension: As per customers' requirements
Copper 0.15 - 0.4
Iron 0 - 0.7
Magnesium 0.8 - 1.2
Manganese 0.15 max
Other 0.15 max
Remainder Each 0.05 max
Silicon 0.4 - 0.8
Titanium 0.15 max
Zinc 0.25 max
The alloy 6061 has very good welding characteristics and may be welded by all of the common welding techniques. Gas tungsten arc welding is generally used for thin sections (less than 0.032") and gas metal arc welding is used for heavier sections.
Commonly 6061 used in the manufacture of heavy-duty structures requiring good corrosion resistance, truck and marine components, railroad cars, furniture, tank fittings, general structural and high pressure applications, wire products, and in pipelines.
We accept to customize the size and quantity.You only need to tell me the alloy,temper,size,quantity that you need,we will produce specially for you.
|Specification||Name: 6000 series Aluminum Sheet|
|Alloy: 6061, 6082, 6063 etc.|
|Temper: O, H112, T4, T6, T651 etc.|
|Width: Up to 1500mm|
|Surface treatment: mill finished, Print marks|
|Feature||Machinability: In the harder T 4 and T6 tempers it is good. It is notably less easy to machine in the annealed temper.|
|Forming: Easily cold worked and formed in the annealed condition. Stamping, bending, spinning, deep drawing are all readily accomplished using standard methods.|
|Welding: It has very good welding characteristics and may be welded by all of the common welding techniques.|
|Heat Treatment: Solution heat treat at 990 F for adequate time to allow for thorough heating and then water quench. Precipitation hardening is done at 320 F for 18 hours and air cool, followed by 350 F for 8 hours and air cooling.|
|Forging: It is capable of being hot forged at temperatures in the range of 900 F to 750 F.|
|Hot Working: Hot working may be done in the temperature range of 700 F to 500 F.|
|Cold Working: Cold working in the O temper condition is readily performed. The alloy is notably less easy to cold form in the T 4 and T 6 tempers.|
|Annealing: Annealing should be done at 775 F for 2 to 3 hours followed by controlled cooling at 50 f per hour down to 500 F, then air cool.|
|Aging: The aging precipitation heat treatment is done at 350 F for 8 hours followed by air cooling. This produces the T6 temper.|
|Application||Commonly used in the manufacture of heavy-duty structures requiring good corrosion resistance, truck and marine components, railroad cars, furniture, tank fittings, general structural and high pressure applications, wire products, pipelines, various toolings etc.|
|Alloy||Chemical Component %≤|
|6061||0.4- 0.8||0.7||0.15-0.4||0.15||0.8- 1.2||0.04-0.35||\||0.25||0.15||0.05||0.15||remainder|
|6082||0.7- 1.3||0.5||0.1||0.4- 1.0||0.6- 1.2||0.25||\||0.2||0.1||0.05||0.15||remainder|