Shandong, China
Business Type:
Manufacturer/Factory
Number of Employees:
69
Year of Establishment:
2003-09-26
Plant Area:
9500 square meters
Average Lead Time:
Peak season lead time: one month
Off season lead time: one month
OEM/ODM Service
Sample Available

Aluminium Cladding Foil, Aluminum Foil, Alu Foil manufacturer / supplier in China, offering China Factory Aluminum Cladding Coil Foil, Aluminum Straight Tube, Profile, Extruded, Extrusion, Radiator, Aluminum Checkered Plate - Five Bar 1060/3003/5052 and so on.

Gold Member Since 2009
Audited Supplier
Supplier Homepage Products Aluminum Coil China Factory Aluminum Cladding Coil Foil

China Factory Aluminum Cladding Coil Foil

Get Latest Price
Min. Order: 1 Ton
Port: Qingdao, China
Production Capacity: 150000 Tons/Year
Payment Terms: L/C, T/T, Western Union, Paypal
Type: Aluminum Coils
Application: Decorations
Shape: Rectangular
Grade: 5000 Series
Surface Treatment: Mill Finish
Technique: Rolling

You Might Also Like

Loading...

Basic Info

Model NO.: 5052
Alloy: Alloy
Temper: O - H112
Certification: ASTM, GB/T
Trademark: BAODI
Transport Package: Wooden Pallet, Veneer Pallet
Specification: GB/T 3880-2006
Origin: China
HS Code: 7606711

Product Description

SpecificationName: 5000 series Aluminum Coil
Alloy: 5052, 5005, 5754, 5083 etc.
Temper: O, H12, H22, H32, H14, H24, H26, H18, H112 etc.
Thickness: 0.2-5mm
Width: Up to 1800mm
Coil weight: 5-6tons
Surface treatment: mill finished, anodized, embossed, PVC coated
FeatureMachinability: It has relatively fair machinability. It is easier to machine in the hard temper than as annealed and the quality of finish is better if machined in the hard condition. Oil lubricants should be used for machining, except that very light cuts may be done dry.
Forming: It is readily formed at room temperature. Successive cold working decreases the formability.
Heat Treatment: It cannot be hardened by means of heat treatment. It does harden due to cold working.
Forging: It may be forged in the temperature range of 950 F down to 500 F
Cold Working: The alloy cold works readily and may be formed by drawing or spinning. However the amount of cold work imparted by spinning makes intermediate annealing necessary.
Annealing: Anneal at 650 F and air cool.
Hardening: Hardens only from cold working.
Applicationhydraulic tubes, kitchen cabinets, small boats, home freezers, milk crates, aircraft tube, fencing, small boats, gas lines, refrigerator panels, utensils, welded pressure vessels, marine, auto aircraft cryogenics, drilling rigs, TV towers, transportation equipment, missile components etc.
AlloyChemical Component %≤
SiFeCuMnMgCrNiZnTiothersAl
singletotal
50520.250.40.10.12.2-2.80.15-0.3\0.1\0.050.15remainder
50050.30.70.20.20.5-1.10.1\0.25\0.050.15remainder
57540.40.40.10.52.6-3.60.3\0.20.150.050.15remainder
50830.40.40.10.4-1.04.0-4.90.05-0.25\0.250.150.050.15remainder
ContactMs. Margaret Tel: 0086-15553544561

Send your message to this supplier

*From:
*To:
avatar Ms. Fiona Fan
*Message:

Enter between 20 to 4,000 characters.

This is not what you are looking for? Post a Sourcing Request Now