Aluminum Plate, Aluminum Plates, Aluminium Plate manufacturer / supplier in China, offering Quenched Aluminum Mould Plate 6082 T651, Rolled Aluminium Sheet and Plate Metal 6061 6082 T6 T651 4′*8′ for Tooling Mould CNC From China Supplier Factory Price, Rolled Alloy Aluminium Sheet and Plate 6061 6082 T6 T651 4′*8′ for Tooling Mould From China Supplier Factory Price and so on.

(/ )

Supplier Homepage Product Aluminum Thick Plate Quenched Aluminum Mould Plate 6082 T651

Quenched Aluminum Mould Plate 6082 T651

FOB Price: Get Latest Price
Min. Order: 1 Ton
Production Capacity: 150, 000 Tons/Year
Transport Package: Wooden Pallet /Plywood Pallet /Steel Frame Pallet
Payment Terms: L/C, T/T, Western Union, Paypal, Money Gram

Request a custom order and have something just for you!

Send Customized Request
Basic Info
  • Model NO.: 6082
  • Application: Mould, Structure, Industrial
  • Grade: 6000 Series
  • Technique: DC
  • Temper: T3 - T8
  • Sample: Free
  • Specification: SGS, ROHS
  • HS Code: 76061290
  • Type: Aluminum Sheets
  • Shape: Rectangular
  • Surface Treatment: Quenched
  • Alloy: Alloy
  • Certification: ASTM, JIS, GB/T
  • Trademark: Baodi
  • Origin: China
Product Description
We offer aluminum thick plate 6082 T6 and T651
Thickness: Above 6mm to 200mm
Width: 1525mm mx
Length: As per requirements
Temper: T6, T651

Chemical composition is

Aluminium Balance
Copper 0.15 - 0.4
Iron 0 - 0.7
Magnesium 0.8 - 1.2
Manganese 0.15 max
Other 0.15 max
Remainder Each 0.05 max
Silicon 0.4 - 0.8
Titanium 0.15 max
Zinc 0.25 max

Probably the most commonly available, heat treatable aluminum alloy.
Commonly used in the manufacture of heavy-duty structures requiring good corrosion resistance, truck and marine components, railroad cars, furniture, tank fittings, general structural and high pressure applications, wire products, and in pipelines.

SpecificationName: 6000 series Aluminum Sheet
Alloy: 6061, 6082, 6063 etc.
Temper: O, H112, T4, T6, T651 etc.
Thickness: 6-200mm
Width: Up to 1500mm
Surface treatment: mill finished, Print marks
FeatureMachinability: In the harder T 4 and T6 tempers it is good. It is notably less easy to machine in the annealed temper.
Forming: Easily cold worked and formed in the annealed condition. Stamping, bending, spinning, deep drawing are all readily accomplished using standard methods.
Welding: It has very good welding characteristics and may be welded by all of the common welding techniques.
Heat Treatment: Solution heat treat at 990 F for adequate time to allow for thorough heating and then water quench. Precipitation hardening is done at 320 F for 18 hours and air cool, followed by 350 F for 8 hours and air cooling.
Forging: It is capable of being hot forged at temperatures in the range of 900 F to 750 F.
Hot Working: Hot working may be done in the temperature range of 700 F to 500 F.
Cold Working: Cold working in the O temper condition is readily performed. The alloy is notably less easy to cold form in the T 4 and T 6 tempers.
Annealing: Annealing should be done at 775 F for 2 to 3 hours followed by controlled cooling at 50 f per hour down to 500 F, then air cool.
Aging: The aging precipitation heat treatment is done at 350 F for 8 hours followed by air cooling. This produces the T6 temper.
ApplicationCommonly used in the manufacture of heavy-duty structures requiring good corrosion resistance, truck and marine components, railroad cars, furniture, tank fittings, general structural and high pressure applications, wire products, pipelines, various toolings etc.
 
AlloyChemical Component %≤
SiFeCuMnMgCrNiZnTiothersAl
singletotal
60610.4- 0.80.70.15-0.40.150.8- 1.20.04-0.35\0.250.150.050.15remainder
60820.7- 1.30.50.10.4- 1.00.6- 1.20.25\0.20.10.050.15remainder
60630.2-
0.6
0.350.10.10.45-0.90.1\0.10.10.050.15remainder
ContactMs. Cherry Xia Tel: 0086-15106464366

Send your message to this supplier
Avatar
Ms. Tracy
*From:
To: Ms. Tracy
*Message:

Enter between 20 to 4,000 characters.

This is not what you are looking for? Post a Sourcing Request Now

Find Similar Products By Category