Aluminium Sheet, Aluminum Plate, Aluminum Block manufacturer / supplier in China, offering Building Material 5083 H116 H32 Marine /Mould Sheet, PVC Cover Mill Finish Aluminum Sheet, 1050, 1060, 1100, 3003, 5052 Aluminum Alloy Sheet/Coil Metal and so on.

(/ )

Supplier Homepage Product Aluminum Thick Plate Building Material 5083 H116 H32 Marine /Mould Sheet

Building Material 5083 H116 H32 Marine /Mould Sheet

FOB Price: Get Latest Price
Min. Order: 1 Ton
Production Capacity: 150, 000 Tons/Year
Transport Package: Wooden Pallet /Plywood Pallet /Steel Frame Pallet
Payment Terms: L/C, T/T

Request a custom order and have something just for you!

Send Customized Request
Basic Info
  • Model NO.: 5083
  • Application: Transportation Tools, Tire Moulds, Shoe Moulds
  • Grade: 5000 Series
  • Technique: Extruded
  • Temper: O - H112
  • Material: Aluminum Alloy
  • Specification: ROHS, SGS
  • HS Code: 760612
  • Type: Aluminum Sheets
  • Shape: Rectangular
  • Surface Treatment: Mill Finish
  • Alloy: Alloy
  • Certification: ASTM, JIS, GB/T
  • Trademark: Baodi
  • Origin: China
Product Description
Aluminum Block 5052 5083 H112
Our Sheet is greatly used in hydraulic tubes, kitchen cabinets, small boats, home freezers, milk crates, aircraft tube, fencing, small boats, gas lines, refrigerator panels, utensils, welded pressure vessels, marine, auto aircraft cryogenics, drilling rigs, TV towers, transportation equipment, missile components etc.
 
SpecificationName: 5000 series Aluminum Sheet
Alloy: 5052, 5083 etc.
Temper: H112
Thickness: 0.2-200mm
Width: Up to 1800mm
Length: up to 6000mm
Surface treatment: mill finished, PVC coated, Print marks
FeatureMachinability: It has relatively fair machinability. It is easier to machine in the hard temper than as annealed and the quality of finish is better if machined in the hard condition. Oil lubricants should be used for machining, except that very light cuts may be done dry.
Forming: It is readily formed at room temperature. Successive cold working decreases the formability.
Heat Treatment: It cannot be hardened by means of heat treatment. It does harden due to cold working.
Forging: It may be forged in the temperature range of 950 F down to 500 F
Cold Working: The alloy cold works readily and may be formed by drawing or spinning. However the amount of cold work imparted by spinning makes intermediate annealing necessary.
Annealing: Anneal at 650 F and air cool.
Hardening: Hardens only from cold working.
Applicationhydraulic tubes, kitchen cabinets, small boats, home freezers, milk crates, aircraft tube, fencing, small boats, gas lines, refrigerator panels, utensils, welded pressure vessels, marine, auto aircraft cryogenics, drilling rigs, TV towers, transportation equipment, missile components etc.
AlloyChemical Component %≤
SiFeCuMnMgCrNiZnTiothersAl
singletotal
50520.250.40.10.12.2-2.80.15-0.3\0.1\0.050.15remainder
50830.40.40.10.4-1.04.0-4.90.05-0.25\0.250.150.050.15remainder
ContactMs. Margaret  Tel: 0086-15553544561

Building Material 5083 H116 H32 Marine /Mould Sheet
Building Material 5083 H116 H32 Marine /Mould Sheet
Building Material 5083 H116 H32 Marine /Mould Sheet
Send your message to this supplier
Avatar
Ms. Margaret Feng
*From:
To: Ms. Margaret Feng
*Message:

Enter between 20 to 4,000 characters.

This is not what you are looking for? Post a Sourcing Request Now

Find Similar Products By Category