Aluminum Plate, Aluminum Plates, Aluminium Plate manufacturer / supplier in China, offering Quality Aluminum Marine Plate (5083), Aluminum Flat and Square Bar, Rod, Brass Coil H65 (C26800) and so on.

(/ )

Supplier Homepage Product Aluminum Thick Plate Quality Aluminum Marine Plate (5083)

Quality Aluminum Marine Plate (5083)

FOB Price: Get Latest Price
Min. Order: 1 Ton
Production Capacity: 150000 Tons/Year
Transport Package: by Wooden Pallets
Payment Terms: L/C, T/T, Western Union

Request a custom order and have something just for you!

Send Customized Request
Basic Info
  • Model NO.: 5083
  • Application: Transportation Tools
  • Grade: 5000 Series
  • Technique: Extruded
  • Temper: O - H112
  • Trademark: Baodi
  • Origin: China
  • Type: Aluminum Sheets
  • Shape: Rectangular
  • Surface Treatment: Mill Finish
  • Alloy: Alloy
  • Certification: ASTM
  • Specification: SGS
  • HS Code: 76061290
Product Description
Aluminum Marine Plate specification:

Alloy: 5083
Temper: O, H112, H24, H12
Thickness: 1.0mm-200.0mm
Width: Up to 2200mm
Length: As per customers' requirements

Chemical composition:
Aluminum Balance
Chromium 0.05 - 0.25
Copper 0.1 max
Iron 0.4 max
Magnesium 4 - 4.9
Manganese 0.4 - 1
Remainder Total 0.15 max
Silicon 0.4 max
Titanium 0.15 max
Zinc 0.25 max

5083 has very good corrosion resistance,  it is easily welded and does have good strength. Commonly be used in the manufacture of unfired, welded pressure vessels, marine, autoaircraft cryogenics, drilling rigs, TV towers, transportation equipment, and in missile components.
 
SpecificationName: 5000 series Aluminum Sheet
Alloy: 5052, 5005, 5754, 5083 etc.
Temper: O, H12, H22, H32, H14, H24, H26, H18, H112 etc.
Thickness: 0.2-200mm
Width: Up to 1800mm
Length: up to 6000mm
Surface treatment: mill finished, PVC coated, Print marks
FeatureMachinability: It has relatively fair machinability. It is easier to machine in the hard temper than as annealed and the quality of finish is better if machined in the hard condition. Oil lubricants should be used for machining, except that very light cuts may be done dry.
Forming: It is readily formed at room temperature. Successive cold working decreases the formability.
Heat Treatment: It cannot be hardened by means of heat treatment. It does harden due to cold working.
Forging: It may be forged in the temperature range of 950 F down to 500 F
Cold Working: The alloy cold works readily and may be formed by drawing or spinning. However the amount of cold work imparted by spinning makes intermediate annealing necessary.
Annealing: Anneal at 650 F and air cool.
Hardening: Hardens only from cold working.
Applicationhydraulic tubes, kitchen cabinets, small boats, home freezers, milk crates, aircraft tube, fencing, small boats, gas lines, refrigerator panels, utensils, welded pressure vessels, marine, auto aircraft cryogenics, drilling rigs, TV towers, transportation equipment, missile components etc.
AlloyChemical Component %≤
SiFeCuMnMgCrNiZnTiothersAl
singletotal
50520.250.40.10.12.2-2.80.15-0.3\0.1\0.050.15remainder
50050.30.70.20.20.5-1.10.1\0.25\0.050.15remainder
57540.40.40.10.52.6-3.60.3\0.20.150.050.15remainder
50830.40.40.10.4-1.04.0-4.90.05-0.25\0.250.150.050.15remainder
ContactMs. Margaret  Tel: 0086-15553544561
Send your message to this supplier
Avatar
Ms. Tracy
*From:
To: Ms. Tracy
*Message:

Enter between 20 to 4,000 characters.

This is not what you are looking for? Post a Sourcing Request Now

Find Similar Products By Category