5052, 5005, 5754, 5083 Plate, Sheet Aluminium, Aluminum Plate
|FOB Price:||Get Latest Price|
|Min. Order:||1 Ton|
|Production Capacity:||150, 000 Metric Tons/Year|
|Transport Package:||Wooden Pallet /Plywood Pallet /Steel Frame Pallet|
|Payment Terms:||L/C, T/T, Western Union|
- Model NO.: 5052, 5005, 5754, 5083
- Certification: ASTM, JIS, GB/T
- Grade: 5000 Series
- Surface Treatment: Mill Finish
- Sample: Free
- Shape: Flat
- Specification: SGS, ROHS
- HS Code: 7606125900
- Application: Decorations, Transportation Tools, Door & Window, Glass Wall, Heat Sink
- Technique: Extruded
- Temper: O - H112
- Alloy: Alloy
- Type: Aluminum Sheets
- Trademark: Baodi
- Origin: China
Features of 5000 series
1. Can be referred to as aluminum and magnesium alloys. Magnesium content between 3-5%.
2. Non-heat-treatable alloy
3. Low density, high tensile strength and elongation rate. Good corrosion resistance, weldability and cold workability.
Technical standard national standard (GB/T 3880-2006)
The application scope of 5083 aluminum plate
5083 aluminum plate is often used in materials for ships, vehicles, cars and aircraft plate weldments pressure vessel, which is to be strict fire prevention, cooling device, television tower, drilling equipment, transportation equipment, missile component and armor.
The chemical composition of 5083 aluminum plate
Al: Aluminum allowance Si: 0.4 or less Cu: 0.1 or less Mg: 4.0-4.9
Zin: 0.25 Mn: 0.40-1.0 Ti: 0.15 or less Cr: 0.05-0.25 Fe: 0.4
Individual: 0.05 Total: 0.15
The mechanical properties of 5083 aluminum plate
Tensile strength: σ B (MPa): 110-136
Elongation delta: δ 10 (%): ≥ 20
Annealing temperature: 415 ° C.
Yield strength: σ S (MPa) ≥ 110
Elongation rate: δ 5 (%) ≥ 12
The application scope of 5052 aluminum plate
5052 aluminum plate is mainly used in the request high plasticity and good weldability, working in a liquid or gas medium low load parts, such as tank, gas or oil duct, and other various liquid containers made of deep drawing parts: Small load wire used for rivet. Also commonly used in the transportation vehicles, ships, sheet metal parts, instrument, lamps stent and rivet, metal products, electrical enclosure, etc.
Chemical composition of 5052
Al: Allowance; Si: 0.25; Cu: 0.10; Mg: 2.2 ~ 2.8;
Zinc: 0.10; Mn: 0.10; Cr: 0.15 ~ 0.35; Fe: 0.4 0.
Mechanical properties of 5052
Tensile strength (σ B ): 170~305MPa
Conditions to yield strength: σ 0.2 (MPa)≥ 65
Modulus of elasticity: (E): 69.3 ~ 70.7 Gpa
Annealing temperature: 345 ° C.
The surface quality
1, the surface is not allowed to have crack, corrosion spots or nitrate.
2, on the surface, allowing a depth of no more than 8% of the nominal size peeling defect part wall thickness, air bubbles, surface roughness and the local mechanical damage, but the defects cannot be more than 0.5 mm, maximum depth defect sheet with a total area of no more than 5% of the total area.
3, allow the supplier polishing along the longitudinal profiles until the surface is smooth.
4, other requirements: Disucssed by both sides.
|Specification||Name: 5000 series Aluminum Sheet|
|Alloy: 5052, 5005, 5754, 5083 etc.|
|Temper: O, H12, H22, H32, H14, H24, H26, H18, H112 etc.|
|Width: Up to 1800mm|
|Length: up to 6000mm|
|Surface treatment: mill finished, PVC coated, Print marks|
|Feature||Machinability: It has relatively fair machinability. It is easier to machine in the hard temper than as annealed and the quality of finish is better if machined in the hard condition. Oil lubricants should be used for machining, except that very light cuts may be done dry.|
|Forming: It is readily formed at room temperature. Successive cold working decreases the formability.|
|Heat Treatment: It cannot be hardened by means of heat treatment. It does harden due to cold working.|
|Forging: It may be forged in the temperature range of 950 F down to 500 F|
|Cold Working: The alloy cold works readily and may be formed by drawing or spinning. However the amount of cold work imparted by spinning makes intermediate annealing necessary.|
|Annealing: Anneal at 650 F and air cool.|
|Hardening: Hardens only from cold working.|
|Application||hydraulic tubes, kitchen cabinets, small boats, home freezers, milk crates, aircraft tube, fencing, small boats, gas lines, refrigerator panels, utensils, welded pressure vessels, marine, auto aircraft cryogenics, drilling rigs, TV towers, transportation equipment, missile components etc.|
|Alloy||Chemical Component %≤|